Calcium aluminates are a range of materialsTaylor H.F.W (1990) Cement Chemistry, Academic Press, , pp. 34–38. obtained by heating calcium oxide and aluminium oxide together at high temperatures. They are encountered in the manufacture of refractories and cements.
The stable phases shown in the phase diagram (formed at atmospheric pressure under an atmosphere of normal humidity) are:
Tricalcium aluminate, 3CaO·Al2O3 () Dodecacalcium hepta-aluminate, 12CaO·7Al2O3 () (once known as mayenite) Monocalcium aluminate, CaO·Al2O3 (CA) (occurring in nature as krotite and dmitryivanovite – two polymorphs) , CaO·2Al2O3 () (occurring in nature as grossite ) Monocalcium hexa-aluminate, CaO·6Al2O3 () (occurring in nature as hibonite, a representative of magnetoplumbite group)
In addition, other phases include:
Dicalcium aluminate, 2CaO·Al2O3 (), which exists only at pressures above 2500 MPa.Taylor H.F.W (1990) Cement Chemistry, Academic Press, , pp. 28, 29. The crystal is orthorhombic, with density 3480 kg·m−3. The natural dicalcium aluminate, brownmillerite, may form at normal pressure but elevated temperature in pyrometamorphic zones, e.g., in burning coal-mining heaps. , 5CaO·3Al2O3 (), forms only under an anhydrous and oxygen free atmosphere. The crystal is orthorhombic, with a density of 3067 kg·m−3. It reacts rapidly with water. , 4CaO·3Al2O3 (), is a metastable phase formed by dehydrating 4CaO·3Al2O3·3H2O ().
Hydration reaction In contrast to Portland cements, calcium aluminates do not release calcium hydroxide () portlandite or lime during their hydration.
See also Calcium aluminate cements Cement Cement chemist notation (CCN)in which the following abbreviations for calcium and aluminium oxides are defined as: C = CaO A = Hydrocalumite Mayenite Ye'elimite, , a rare natural anhydrous calcium sulfoaluminate